Publikováno v:
IEEE Transactions on Appiled Superconductivity. 12:1128-1131
A technique has been developed for testing long lengths of superconducting cable made from BSCCO 2212 wires in liquid nitrogen. The cable is tested as a large diameter spiral with removable voltage taps so that the conductor can be recovered for use
Autor:
D.R. Dietderich, Aoki Yuji, N. Ohtani, Tsutomu Koizumi, R.M. Scanlan, L.R. Motowidlo, R.S. Sokolowski, Takayo Hasegawa, Shigeo Nagaya
Publikováno v:
Physica C: Superconductivity. :2539-2543
An 80 meter long Rutherford cable was fabricated with 20 strands of 0.8 mm diameter Bi-2212 wire. The conductor utilized in this cable was a double stack design (7 × 61) comprising 427 filaments. The critical current (Ic) of the cable was measured a
Autor:
Shigeo Nagaya, L.R. Motowidlo, N. Ohtani, Aoki Yuji, R.M. Scanlan, Takayo Hasegawa, Tsutomu Koizumi, R.S. Sokolowski
Publikováno v:
Physica C: Superconductivity. 335:1-5
We developed a new strong Rutherford cable using Bi 2 Sr 2 CaCu 2 O y (Bi-2212) high temperature superconducting (HTS) wire, which consisted of 427 superconducting filaments and AgMgSb alloy outer sheath. This wire exhibited excellent critical curren
Autor:
K. Card, S. Sengupta, J.R. Gaines, S.M. Mukhopadyay, R.S. Sokolowski, E. Caprino, L.R. Motowidlo, R.R. Garcia
Publikováno v:
IEEE Transactions on Appiled Superconductivity. 9:2601-2604
A chemical precipitation method is utilized to synthesize bismuth-strontium-calcium-copper oxide powder. Tetra-methyl ammonium hydroxide and tetra-methyl ammonium carbonate are used as a precipitant and for pH adjustment. Effect of processing paramet
Autor:
R.S. Sokolowski, Abdulhussain E. Mahdi, A. Power, Yifeng Yang, Pradeep Haldar, R.L. Stoll, C. Beduz, Jan K. Sykulski, T. Hughes
Publikováno v:
IEEE Transactions on Appiled Superconductivity. 7:1658-1661
Self-field ac losses in Ag sheathed PbBi-2223 tapes were measured using a thermometric method, which determines the losses by measuring the temperature profile of a vacuum insulated sample, with both ends at a fixed temperature. In practice, the samp
Publikováno v:
Scripta Metallurgica. 17:569-572
Akademický článek
Tento výsledek nelze pro nepřihlášené uživatele zobrazit.
K zobrazení výsledku je třeba se přihlásit.
K zobrazení výsledku je třeba se přihlásit.
Akademický článek
Tento výsledek nelze pro nepřihlášené uživatele zobrazit.
K zobrazení výsledku je třeba se přihlásit.
K zobrazení výsledku je třeba se přihlásit.
Akademický článek
Tento výsledek nelze pro nepřihlášené uživatele zobrazit.
K zobrazení výsledku je třeba se přihlásit.
K zobrazení výsledku je třeba se přihlásit.