B.S. Gong, Z.J. Zhang, J.P. Hou, R. Liu, Q.Q. Duan, H.W. Wang, X.G. Wang, H.Z. Liu, H. Wang, G. Purcek, M. Demirtas, H. Yanar, Z.F. Zhang
Publikováno v:
Journal of Materials Research and Technology, Vol 29, Iss , Pp 2448-2457 (2024)
To reveal the effects of aging state on the low-cycle fatigue (LCF) performance of 2024 Al alloy, LCF experiments were conducted on the 2024 Al alloy with three aging states (underaged (UA), peak-aging (PA) and overaged (OA)), respectively. It is fou
Externí odkaz:
https://doaj.org/article/d4261f8051d34064a2888c8da595ae60
Autor:
S.L. Lu, Z.J. Zhang, R. Liu, Z. Qu, S.J. Li, X.H. Zhou, Q.Q. Duan, B.N. Zhang, X.M. Zhao, W. Zhao, P. Ramasamy, J. Eckert, Z.F. Zhang
Publikováno v:
Additive Manufacturing. 71:103603
Autor:
Linmiao Li, Q.Q. Duan, Min Song, W.L. Li, Xiaozhou Liao, Xianghai An, J. Gu, A.G. Wang, Z.F. Zhang, Xiaodan Wang
Publikováno v:
Journal of Materials Science & Technology. 39:1-6
The fatigue cracking behavior at twin boundaries (TBs) in a CoCrFeMnNi high-entropy alloy with three different grain sizes was systematically investigated under low-cycle fatigue. Irrespective of grain size, the change from slip band cracking to TB c
Autor:
Dandan Ben, H.J. Yang, Yuang Dong, Yanzhong Tian, Shijie Sun, Lingxiao Meng, Q.Q. Duan, P. Zhang, Zhefeng Zhang
Publikováno v:
SSRN Electronic Journal.
Autor:
Yu Guo, Xi Xie, Zengqian Liu, Longchao Zhuo, Jian Zhang, Shaogang Wang, Q.Q. Duan, Qing Jia, Dake Xu, Weihai Xue, Deli Duan, Filippo Berto, Zhefeng Zhang, Rui Yang
Publikováno v:
SSRN Electronic Journal.
Publikováno v:
SSRN Electronic Journal.
Autor:
D.D. Ben, H.J. Yang, Y.A. Dong, Y.Z. Tian, S.J. Sun, L.X. Meng, Q.Q. Duan, P. Zhang, Z.F. Zhang
Publikováno v:
Materials Characterization. 195:112557
Akademický článek
Tento výsledek nelze pro nepřihlášené uživatele zobrazit.
K zobrazení výsledku je třeba se přihlásit.
K zobrazení výsledku je třeba se přihlásit.
Publikováno v:
Engineering Fracture Mechanics. 211:362-370
In this paper, the fracture toughness and impact toughness were systematically studied in high-strength steels. The results show that the two types of toughness are both the representative of the competition between flat fracture and shear fracture,
Publikováno v:
International Journal of Fatigue. 161:106916