Publikováno v:
Key Engineering Materials. 882:35-49
Corrosion behavior of three carbon steels with increasing galvanized coating thickness of 5.6, 8.4 and 19.2 μm named as T1, T2and T3, respectively, was studied by immersion test, potentiodynamic polarization and electrochemical impedance spectroscop
Publikováno v:
Journal of Sustainable Metallurgy. 7:115-125
Ladle refining is a popular secondary metallurgy process and plays a vital role in achieving the desired chemistry and temperature during steelmaking. The slag produced after ladle refining mostly contains dicalcium silicate (C2S). The presence of hi
Publikováno v:
Journal of Failure Analysis and Prevention. 17:513-521
Gradual build-up of scum over the liquid steel surface in the mould gives rise to entrapped exogenous inclusions and slag patch in the cast billets. The problem is more commonly observed during the open stream casting of continuous casting of high ca
Publikováno v:
steel research international. 93:2100121
This investigation discusses the experimental methods to characterize and evaluate the mold flux performance during continuous casting of liquid steel. The mold fluxes are initially characterized by the conventional techniques for particle size, phas
Publikováno v:
Ironmaking & Steelmaking. 41:547-553
Less critical grades of steel for long products are commonly produced from open cast billets. However, melt spitting from the mould is one of the potential safety hazards and may adversely affect the cast steel quality besides upsetting the caster pr
Publikováno v:
ISIJ International. 49:521-528
Determination of best combination of current and frequency of an electromagnetic stirrer (EMS) of a billet caster is of prime importance for ensuring good internal, surface as well as subsurface quality of billets. In the present study, this optimiza
Autor:
Somnath Basu, Preeti Prakash Sahoo
Publikováno v:
ISIJ International. 46:219-225
Producing a defect free product is most important in the process of continuous casting as the defect may propagate to the end product and also can increase the downgrading. Inadequate oscillation parameters as well as a defective oscillation may grea