Publikováno v:
Surfaces, Vol 7, Iss 3, Pp 550-559 (2024)
The iron (Fe) specimens selected as the substrate metal for this study were surface-treated using fluorine gas, and their wettability with liquid sodium (Na) was evaluated using the sliding angle. Additionally, the surface morphology and binding stat
Externí odkaz:
https://doaj.org/article/a19b31331f1d420eb1fe6f0afd348ddc
Publikováno v:
Colorants, Vol 2, Iss 3, Pp 552-564 (2023)
Surface fluorination with pure F2 gas can easily make the surface on PP (polypropylene) hydrophobic, and it causes limited dyeability, as reported in a previous paper. In this study, to produce a more hydrophilic surface, surface fluorination of PP w
Externí odkaz:
https://doaj.org/article/37d31caf7c4d455dab7898b7315596df
Publikováno v:
Journal of Coatings Technology and Research. 19:617-624
The surface of polycarbonate (PC) was fluorinated with a mixed gas of F2 and O2 at 25 °C for 1 h. The surface roughness (Ra) of the fluorinated PC samples was about double that of the untreated sample (0.685 nm), while the water contact angle of the
Publikováno v:
Colorants; Volume 1; Issue 2; Pages: 121-131
The surface of polypropylene (PP) was modified with fluorine gas at 25 °C and 10–380 Torr for 1 h. The surface roughness of the fluorinated PP samples was approximately two times larger than that (5 nm) of the untreated sample. The results of Four
Publikováno v:
Journal of Fluorine Chemistry. :110012
Publikováno v:
Journal of Fluorine Chemistry. 224:73-79
The reaction mechanism between 0.1 MPa ClF3 gas and Ni was investigated in the temperature range of 473–873 K for 0–120 h. The kinetic corrosion behavior of Ni metal under 0.1 MPa ClF3 gas changed markedly at the point of 823 K. The reaction temp
Publikováno v:
Composites Communications. 10:205-208
To improve the adhesion between polymer matrix and metal plating films, PET surface was modified with F 2 gas at 25 ℃ and 10–760 Torr for 1 h. The surface of fluorinated PET became markedly clouded after ethanol washing. The surface roughness (Ra