Lesniak, D., Zaborowski, K., Madura, J., Gromek, P., Leszczynska-Madej, B., Woznicki, A., Zasadzinski, J., Libura, W., Jurczak, H.
Publikováno v:
In Procedia Manufacturing 2019 27:144-151
Publikováno v:
Archives of Metallurgy and Materials, Vol 62, Iss 2, Pp 747-755 (2017)
A conventional powder metallurgy method (PM) was used to produce Al-SiC and Al4Cu alloy matrix composites with 2.5, 5, 7.5 and 10 wt% of SiC particles. Two different sizes of the reinforcing phase particles were applied to determine their effect on c
Externí odkaz:
https://doaj.org/article/f693086668dd4b80a9c92c27a51f98cd
Autor:
Leszczyńska-Madej B., Madej M.
Publikováno v:
Archives of Metallurgy and Materials, Vol 61, Iss 4, Pp 1861-1868 (2016)
The results of tribological tests and microstructure examinations of tin babbit with 1.5 % Pb addition after heat treatment are presented in this paper. The specimens were annealed at 150°C for 2, 8, 24 and 48 hours and then tested for wear resistan
Externí odkaz:
https://doaj.org/article/bfe5e7febe5245f58ec8d41035468ccb
Akademický článek
Tento výsledek nelze pro nepřihlášené uživatele zobrazit.
K zobrazení výsledku je třeba se přihlásit.
K zobrazení výsledku je třeba se přihlásit.
Akademický článek
Tento výsledek nelze pro nepřihlášené uživatele zobrazit.
K zobrazení výsledku je třeba se přihlásit.
K zobrazení výsledku je třeba se přihlásit.
Akademický článek
Tento výsledek nelze pro nepřihlášené uživatele zobrazit.
K zobrazení výsledku je třeba se přihlásit.
K zobrazení výsledku je třeba se přihlásit.
Akademický článek
Tento výsledek nelze pro nepřihlášené uživatele zobrazit.
K zobrazení výsledku je třeba se přihlásit.
K zobrazení výsledku je třeba se přihlásit.
Publikováno v:
Archives of Metallurgy and Materials, Vol 61, Iss 3, Pp 1663-1670 (2016)
The influence of cooling rate after homogenization on the 2017A alloy microstructure was analysed. The capability of the θ (Al2Cu) particles, precipitated during various homogenization coolings, for rapid dissolution was estimated. For this purpose,
Externí odkaz:
https://doaj.org/article/ad766ae49b5e42e9a8f2547c0d9487cd
Publikováno v:
Archives of Metallurgy and Materials, Vol 61, Iss 3, Pp 1575-1580 (2016)
The present study attempts to apply HE to 99.99% pure copper. The microstructure of the samples was investigated by both light microscopy and scanning transmission electron microscopy (STEM). Additionally, the microhardness was measured, the tensile
Externí odkaz:
https://doaj.org/article/6b12a54f7f4946beb6331556c30d9687
Publikováno v:
Archives of Metallurgy and Materials, Vol 60, Iss 3, Pp 1763-1772 (2015)
The paper presents the results of laboratory homogenization investigations of the 6082 grade alloys, differing in Mg and Si content. At the first stage, the microstructure of alloys was analysed after homogenization finished with water quenching. SEM
Externí odkaz:
https://doaj.org/article/77a23e7a53284490a7f64c126a288434