Publikováno v:
Corrosion Science. 80:350-358
Two-dimensional and three-dimensional crack morphologies of stress corrosion cracking (SCC) were studied by serial-sectioning and synchrotron-based X-ray computed tomography. Discontinuous surface cracks were actually continuous inside the specimen,
Externí odkaz:
https://explore.openaire.eu/search/publication?articleId=doi_________::fe7d06c64f0e24c7f1d02439f81029b2
https://doi.org/10.1016/j.corsci.2013.11.057
https://doi.org/10.1016/j.corsci.2013.11.057
Publikováno v:
Corrosion Science. 77:360-368
Pitting and crack nucleation at the early stages of stress corrosion cracking (SCC) under ultra-low elastic load were studied. Pits initiated on the sample surface and grew faster in the thickness direction rather than other directions. This correspo
Externí odkaz:
https://explore.openaire.eu/search/publication?articleId=doi_________::51b2e8a71f49840ec7d7041ebeaef391
https://doi.org/10.1016/j.corsci.2013.08.028
https://doi.org/10.1016/j.corsci.2013.08.028
Publikováno v:
Engineering Failure Analysis. 34:379-386
Tube-sheet cracking is a severe problem in the oil refinery industry with the consequences of shortened service life and increased costs. In this study, the mechanisms of the tube-sheet cracking in slurry oil steam generators have been investigated u
Externí odkaz:
https://explore.openaire.eu/search/publication?articleId=doi_________::6159f7f12a0f8cbd4352cc930321b545
https://doi.org/10.1016/j.engfailanal.2013.08.007