Shi, Yitong, Joseph, Sudha, Saunders, Edward A., Sandala, Rebecca S., Walker, Adrian, Lindley, Trevor C., Dye, David
The mechanism of AgCl-induced stress corrosion cracking of Ti-6246 was examined at \SI{500}{\mega\pascal} and \SI{380}{\celsius} for \SI{24}{\hour} exposures. SEM and STEM-EDX examination of a FIB-sectioned blister and crack showed that metallic Ag w
Externí odkaz:
http://arxiv.org/abs/2010.13875
Cast and HIP'ed \textgamma-TiAl 4522XD is being developed for use in jet engine low pressure turbine blades, where temperature variations occur through the flight cycle. The effects of temperature variations on fatigue cracking were therefore examine
Externí odkaz:
http://arxiv.org/abs/2007.04764
Publikováno v:
Int. J. Plasticity, 102743, 2020
The dislocation structures appearing in highly mis-oriented soft/hard grain pairs in near-alpha titanium alloy Ti6242Si were examined with and without the application of load holds (dwell) during fatigue. Dislocation pile-up in a soft grain resulted
Externí odkaz:
http://arxiv.org/abs/1905.11714
Dislocation interactions at the crack nucleation site were investigated in near-alpha titanium alloy Ti-6242Si subjected to low cycle fatigue. Cyclic plastic strain in the alloy resulted in dislocation pile-ups in the primary alpha grains, nucleated
Externí odkaz:
http://arxiv.org/abs/1806.06367
Hot salt stress corrosion cracking in Ti 6246 alloy has been investigated to elucidate the chemical mechanisms that occur. Cracking was found to initiate beneath salt particles in the presence of oxidation. The observed transgranular fracture was sus
Externí odkaz:
http://arxiv.org/abs/1802.06045
Autor:
Shi, Yitong, Joseph, Sudha, Saunders, Edward A., Sandala, Rebecca S., Walker, Adrian, Lindley, Trevor C., Dye, David *
Publikováno v:
In Corrosion Science 15 July 2021 187
Publikováno v:
In Materials Science & Engineering A 4 November 2020 798
Publikováno v:
In International Journal of Plasticity January 2018 100:90-103
Publikováno v:
In Materials Science & Engineering A 5 January 2016 650:28-37