A Twinning Induced Plasticity (TWIP) steel with a nominal composition of Fe-16.4Mn-0.9C-0.5Si-0.05Nb-0.05V was deformed to an engineering strain of 6\%. The strain around the deformation twins were mapped using the 4D-STEM technique. Strain mapping s
Externí odkaz:
http://arxiv.org/abs/2209.15522
A medium Mn steel of composition Fe-4.8Mn-2.8Al-1.5Si-0.51C (wt.\%) was processed to obtain two different microstructures representing two different approaches in the hot rolling mill, resulting in equiaxed vs. a mixed equiaxed and lamellar microstru
Externí odkaz:
http://arxiv.org/abs/2204.05388
A novel concept of varying the strain hardening rate of a medium Mn steel with 8 wt\% Mn by varying the duration of the intercritical anneal after hot rolling was explored. It was found that the stability of the austenite phase showed an inverse squa
Externí odkaz:
http://arxiv.org/abs/2112.12115
A steel with nominal composition Fe-28Mn-8Al-1.0C in mass percent was hot rolled at two temperatures, 1100 \degree C and 850 \degree C and subsequently aged at 550 \degree C for 24 h. The lower temperature rolling resulted in a yield strength increme
Externí odkaz:
http://arxiv.org/abs/2112.01172
Two ingots weighing 400 g and 5 kg with nominal compositions of Fe-8Mn-4Al-2Si-0.5C-0.07V-0.05Sn were produced to investigate the effect of processing variables on microstructure development. The larger casting has a cooling rate more representative
Externí odkaz:
http://arxiv.org/abs/2110.12729
We measure the stress state in and around a deformation nanotwin in a twinning-induced plasticity (TWIP) steel. Using four-dimensional scanning transmission electron microscopy (4D-STEM), we measure the elastic strain field in a 68.2-by-83.1 nm area
Externí odkaz:
http://arxiv.org/abs/2004.03982
Autor:
Kwok, T W J, Rahman, K M, Xu, X, Bantounas, I, Kelleher, J F, Daswari, S, Alam, T, Banerjee, R, Dye, D
Publikováno v:
Mater. Sci. Eng. A 782:139258, 2020
A novel medium Mn steel of composition Fe-12Mn-4.8Al-2Si-0.32C-0.3V was manufactured with 1.09 GPa yield strength, 1.26 GPa tensile strength and 54% elongation. The thermomechanical process route was designed to be industrially translatable and consi
Externí odkaz:
http://arxiv.org/abs/1908.07258
Akademický článek
Tento výsledek nelze pro nepřihlášené uživatele zobrazit.
K zobrazení výsledku je třeba se přihlásit.
K zobrazení výsledku je třeba se přihlásit.
Akademický článek
Tento výsledek nelze pro nepřihlášené uživatele zobrazit.
K zobrazení výsledku je třeba se přihlásit.
K zobrazení výsledku je třeba se přihlásit.
Akademický článek
Tento výsledek nelze pro nepřihlášené uživatele zobrazit.
K zobrazení výsledku je třeba se přihlásit.
K zobrazení výsledku je třeba se přihlásit.