Stein, Tobias, Wicke, Marcel, Brueckner-Foit, Angelika, Kirsten, Tina, Zimmermann, Martina, Buelbuel, Fatih, Christ, Hans-Jürgen
The near-threshold behavior of long cracks is studied in this paper using precracked flat dogbone specimens of a commercial aluminum alloy in peak-aged and overaged conditions. After introducing the initial crack in compression precracking, the crack
Externí odkaz:
https://tud.qucosa.de/id/qucosa%3A70663
https://tud.qucosa.de/api/qucosa%3A70663/attachment/ATT-0/
https://tud.qucosa.de/api/qucosa%3A70663/attachment/ATT-0/
Autor:
Kirsten Tina, Bülbül Fatih, Wicke Marcel, Christ Hans-Jürgen, Brückner-Foit Angelika, Zimmermann Martina
Publikováno v:
MATEC Web of Conferences, Vol 165, p 20005 (2018)
In the present study two different aluminium alloys, the precipitation hardening alloy EN AW 6082 (peak-aged and overaged) and the work-hardening alloy EN AW 5083 (soft annealed) were examined. Fatigue cracks were initiated by means of a focused ion
Externí odkaz:
https://doaj.org/article/def0890eeee1444481f7a5c7e68717fd
Autor:
Wicke Marcel, Brueckner-Foit Angelika, Kirsten Tina, Zimmermann Martina, Buelbuel Fatih, Christ Hans-Juergen
Publikováno v:
MATEC Web of Conferences, Vol 165, p 13007 (2018)
The near-threshold behavior of long cracks is evaluated using pre-cracked flat dogbone specimens of a commercial aluminum alloy in two heat treatment states. Once the threshold was known, the crack initially introduced by cyclic compression was propa
Externí odkaz:
https://doaj.org/article/91319a1c35334680b98887bc6e1ea99f
Autor:
Bülbül Fatih, Kirsten Tina, Wicke Marcel, Zimmermann Martina, Brückner-Foit Angelika, Christ Hans-Jürgen
Publikováno v:
MATEC Web of Conferences, Vol 165, p 20007 (2018)
Investigations have shown that in the regime of Very High Cycle Fatigue (VHCF) “natural” crack initiation often takes place underneath the material surface leading to crack propagation without contact to atmospheric components. In order to elucid
Externí odkaz:
https://doaj.org/article/151429244ce3439faca7648dcb90e53a
Akademický článek
Tento výsledek nelze pro nepřihlášené uživatele zobrazit.
K zobrazení výsledku je třeba se přihlásit.
K zobrazení výsledku je třeba se přihlásit.