Publikováno v:
Alloys, Vol 3, Iss 2, Pp 140-160 (2024)
In this investigation, the effects of different annealing temperatures (180, 200, 220, 240, 260, and 280 °C) on the microstructure evolution and properties of an extruded Mg–2.0Zn–1.0Y–0.5Zr (wt%) magnesium alloys were determined. Optical micr
Externí odkaz:
https://doaj.org/article/ae5e9ac3be374740b1d51957930cf894
Autor:
Guan Li, Rong Liu, Rongfang Xu, Rajeev K. Varshney, Hanfeng Ding, Mengwei Li, Xin Yan, Shuxian Huang, Juan Li, Dong Wang, Yishan Ji, Chenyu Wang, Junguang He, Yingfeng Luo, Shenghan Gao, Pengcheng Wei, Xuxiao Zong, Tao Yang
Publikováno v:
Crop Journal, Vol 11, Iss 1, Pp 132-139 (2023)
Pea (Pisum sativum L.) is an annual cool-season legume crop. Owing to its role in sustainable agriculture as both a rotation and a cash crop, its global market is expanding and increased production is urgently needed. For both technical and regulator
Externí odkaz:
https://doaj.org/article/b2f9eeeeeed74dca81a798db0af555c8
Publikováno v:
Materials, Vol 13, Iss 4, p 836 (2020)
Microstructure and corrosion behavior of the solution-treated Mg-1.8Zn-1.74Gd-0.5Y-0.4Zr (wt%) alloy were studied. The results of microstructure indicated that the second phases of as-cast alloy was mainly comprised of Mg12Zn(Gd,Y) phase, Mg3Zn3(Gd,Y
Externí odkaz:
https://doaj.org/article/2dcc84117b90413da5691c13ba24ebef
Publikováno v:
Advanced Engineering Materials.
Publikováno v:
Materials and Corrosion. 73:587-601
Publikováno v:
Materials and Corrosion. 73:414-426
Publikováno v:
Journal of Materials Science. 55:1813-1825
This study investigated the microstructure, mechanical properties, corrosion behavior of as-cast Mg–1.8Zn–0.4Zr–1.74Gd–xY (x = 0, 0.25, 0.5, 0.75, 1.0, 1.25 wt%) biodegradable magnesium alloys. Microstructures of the alloys were characterized
Publikováno v:
Procedia Manufacturing. 37:2-7
Hot deformation behavior of cast 5052 aluminum alloy was investigated at the temperature between 300°C and 500°C and the strain rate range from 0.01 s-1 to 10 s-1 by hot compression tests. The constitutive model was established through the flow str
Publikováno v:
Procedia Manufacturing. 37:153-158
Rolling edge crack of 5052 aluminum alloy under one-pass (reductions of 35%, 40%, 50%, 60%, respectively) and multi-pass rolling at total reductions of 60% (two-pass, three-pass, four-pass and five-pass, respectively) at room temperature was analyzed