Journal of Failure Analysis and Prevention. 20:153-158
The leakage of a methanator that made by 304H was analyzed. Near the lugs of the reactor, two cracks without any ductility were found in the hoop direction. From the cross-sectional view of the reactor pipe, more cracks were observed. The cracks were
Publikováno v:
Journal of Failure Analysis and Prevention. 19:958-966
Three cylinders of a long-tube trailer leaked during an inspection and typical quality test. Thus, failure analysis was performed to determine the cause of failure. Macroscopic observation, metallographic analysis, and fracture analysis were implemen
Publikováno v:
Journal of Ocean University of China. 18:177-184
The impact of water temperature (24, 27, 30 and 33°C) and salinity (15, 20, 25, 30 and 33) on oxygen consumption (OCR) and ammonium excretion rate (AER) of ♀ Epinephelus fuscoguttatus × ♂ E. lanceolatus hybrid grouper juveniles (9.39 ± 0.07 g)
Autor:
Jianming Zhai, Xue-xin Shang, Ling-chen Kong, Ming Song, Han-kui Wang, Tong Xu, Yonghui Sun, Haiyang Yu
Publikováno v:
Journal of Failure Analysis and Prevention.
Failure of pump shaft (P116-1) of high-pressure water pump occurred during coke removal. Shaft material (3Cr13) demonstrated yield and tensile strength of 737 and 910 MPa, respectively. Failure analysis was performed to determine the cause of failure