Selected, peer reviewed papers from the 12th International Symposium on Advanced Materials, 26-30 September, 2011, Islamabad, Pakistan
Publikováno v:
Key Engineering Materials. 778:9-15
A series of experiments were conducted to optimize the welding of similar and dissimilar alloys i.e AISI-321 with AISI-321, Inconel-X750 with AISI-321 and Inconel-X750 with Inconel-X750. Single phase rectification type resistance spot welding machine
Publikováno v:
Key Engineering Materials. 778:245-250
An investigation of distress of hot section nozzle guiding vane (NGV) was carried out. Thermal barrier coatings (TBCs) were applied to the components of gas turbine engines to operate at higher temperatures i.e. up to 1200°C. The cause of failure wa
Autor:
Iftichar Us Salam, Khalid Mehmood, Rajdeep Singh Rawat, Mohammad Mujahid, Muhammad Khalid, Aamer Nusair Khan
Publikováno v:
Key Engineering Materials. :547-553
Alumina was coated on Ti6Al4V alloy by atmospheric plasma spraying. Surface and cross sectional analysis of the coating by SEM showed that diameter and thickness of splat was greatly influenced by arc current and stand-off distance. In turn, this var
Publikováno v:
Key Engineering Materials. :206-213
The pressure bulkhead of a passenger aircraft ruptured when the aircraft was cruising at a height of 28,000 ft. Because of the sudden rupture, the rear toilets disintegrated and things like toilet rolls, tissue papers, towels, were sucked into the st
Publikováno v:
Journal of Mechanical Science and Technology. 23:1261-1269
In present study, as a basic step for modeling the fatigue behavior of an extruded Al alloy cylinder, the fatigue crack growth data of the alloy was collected in two orientations. Microstructural analysis revealed that the material had recrystallized
Publikováno v:
IOP Conference Series: Materials Science and Engineering. 146:012010
A two-fold approach was adopted to understand the fatigue crack growth process in an Aluminum alloy; fatigue crack growth test of samples and analysis of fractured surfaces. Fatigue crack growth tests were conducted on middle tension M(T) samples pre
Selected, peer reviewed papers from the 11th International Symposium on Advanced Materials, 08 –12 August, 2009, Islamabad, Pakistan