Publikováno v:
Journal of Advanced Dielectrics, Vol 13, Iss 05 (2023)
CaCu3Ti4[Formula: see text] (CCTO) is a potential dielectric material with giant permittivity, good stability over the wide temperature and frequency range. However, the dielectric responses of CCTO-based ceramics are mainly investigated in the frequ
Externí odkaz:
https://doaj.org/article/55a6fb29b59f470a8a78c8d207b90c11
Autor:
B. Da, X. Liu, J.M. Gong, Z.H. Zhang, Z.J. Ding, N.T. Cuong, J. Hu, J.W. Liu, Z.S. Gao, H.X. Guo, H.X. Wang, H. Zhang, Y. Harada, H. Yoshikawa, S. Tanuma
Publikováno v:
Applied Surface Science. 596:153616
Autor:
S.Z. Zheng, Xiangli Zhong, W.Z. Yan, Shengsheng Yang, Wang Guangyi, Hongjia Song, H.X. Guo, Yuxiong Xue, Jinbin Wang
Publikováno v:
Materials Chemistry and Physics. 219:340-346
Here, the Ag/amorphous Bi3.15Nd0.85Ti3O12/Pt resistive switching memories were designed and prepared, and the total ionizing dose (TID) effects of 60Co γ-ray on the Ag/amorphous Bi3.15Nd0.85Ti3O12/Pt resistive switching memories were investigated. T
Akademický článek
Tento výsledek nelze pro nepřihlášené uživatele zobrazit.
K zobrazení výsledku je třeba se přihlásit.
K zobrazení výsledku je třeba se přihlásit.
Akademický článek
Tento výsledek nelze pro nepřihlášené uživatele zobrazit.
K zobrazení výsledku je třeba se přihlásit.
K zobrazení výsledku je třeba se přihlásit.
Akademický článek
Tento výsledek nelze pro nepřihlášené uživatele zobrazit.
K zobrazení výsledku je třeba se přihlásit.
K zobrazení výsledku je třeba se přihlásit.
Publikováno v:
Corrosion Science. 53:432-440
Erosion-enhanced corrosion of carbon steel in passive state during slurry impingement is dominated by the competition between fresh surface generation and repassivation. The presence of chloride retards repassivation. The average corrosion rate is qu
Publikováno v:
Journal of Colloid and Interface Science. 322:478-484
The effects of plasticizers, pH, and electrolytes on film formation and physical stability of aqueous film coating dispersions (pseudolatexes) of zein were evaluated. The influence of plasticizer on film formation mechanism and minimum film-formation
Publikováno v:
Electrochimica Acta. 52:1108-1116
The erosion-enhanced corrosion of carbon steel A1045 was investigated by electrochemical methods in three borate buffer solutions with different concentrations, and the resistance of material to erosion-enhanced corrosion was discussed from the passi
Publikováno v:
Electrochemistry Communications, Vol 8, Iss 7, Pp 1092-1098 (2006)
An in situ nanoindentation technique was used to study the mechanical property degradation in the surface layer induced by electrochemical dissolution. The load–depth curves of indentation were measured using pure iron immersed in electrolyte. The