Publikováno v:
Procedia Computer Science. 219:486-494
Publikováno v:
Additive Manufacturing. 63:103420
Publikováno v:
Polymer Degradation and Stability. 204:110095
Publikováno v:
Polymer Degradation and Stability. 166:353-378
Polymer aging under combined radiation-thermal oxidative conditions is intrinsically more convoluted than traditional thermal degradation. Accelerated aging methods for predictive purposes have to include thermal as well as radiative degradation path
Autor:
Mathew Celina, Erik Linde
Publikováno v:
Polymer Degradation and Stability. 162:213-223
The application, continued performance, and degradation behavior of polymers often depends on their interaction with small organic or gaseous volatiles. Understanding the underlying permeation and diffusion properties of materials is crucial for pred
Publikováno v:
npj Materials Degradation, Vol 3, Iss 1, Pp 1-8 (2019)
Polymers experience degradation during storage and service. One of the main degradation mechanisms of plasticised-polymer products is the loss of plasticiser, which leads to poorer mechanical properties and eventual contamination of the surrounding e
Publikováno v:
Polymer Degradation and Stability. 189:109598
Polymer degradation under oxidative conditions, particularly under accelerated stresses such as increased temperatures and irradiation, often exhibits spatially heterogeneous oxidation profiles. This well-known behavior is the result of diffusion-lim
Publikováno v:
Polymer Degradation and Stability. 188:109550
The most revealing indicator for oxidative processes or state of degraded plastics is usually carbonyl formation, a key step in materials degradation as part of the carbon cycle for man-made materials. Hence, the identification and quantification of
Autor:
Mikael S. Hedenqvist, Dirk W. Schubert, Thomas Sigl, Erik Linde, Jonas Daenicke, Raymund E. Horch
Publikováno v:
AIP Conference Proceedings.
Driven by the continuing discussion on safety and quality of silicone breast implants, they have turned into focus of this study with respect to the diffusivity of low molar mass components from the silicone gel filling into the silicone breast impla
Autor:
Payam Pourmand, Ulf W. Gedde, Erik Linde, Mikael S. Hedenqvist, Sergey V. Dvinskikh, István Furó
Publikováno v:
Polymer Testing. 53:77-84
The changes occurring in EPDM cable transit seals during thermal ageing and the causes of these changes were investigated. Samples were aged at a temperature of 170 °C, and subsequently evaluated with respect to the distance from the surface with mo