Publikováno v:
Applied Ergonomics. 88:103177
We developed a new kit to assemble three-dimensional (3D) tactile maps for orientation and mobility (O&M) training provided to persons with visual impairments. This study evaluated the effects of verbal explanations combined with 3D tactile map kits
Publikováno v:
Journal of the European Ceramic Society. 21:1269-1272
The room temperature strength of β-sialon with z=0.5 fabricated using a mixture of fine grain size Al2O3 and Si3N4 powders was measured, and the effect of a small, amount of Al(Oi-Pr)3 addition as a dispersant on its strength was also investigated.
Publikováno v:
Journal of Materials Science. 35:863-872
The oxidation behavior of Mo≤5Si3C≤1 and its composites was studied in air over the temperature range of 500°C–1600°C. Experiments revealed poor oxidation resistance of monolithic Mo≤5Si3C≤1 at high temperature. The oxidation was quite ra
Autor:
Kazuhisa Shobu, Kazushi Kishi, Eiji Tani, Annika Kristffersson, Seiki Umebayashi, Robert Pompe
Publikováno v:
Journal of the European Ceramic Society. 18:2015-2018
The room temperature strength of β-sialon fabricated using a mixture of sedimented and flocculated Si3N4, and Al2O3 powders was investigated, in comparison with that achieved using Si3N4 and aluminum iso-propoxide solution, and that using as-mixed S
Publikováno v:
Key Engineering Materials. :225-228
Publikováno v:
Key Engineering Materials. :325-330
Autor:
Kazuhisa Shobu, Eiji Tani
Publikováno v:
Journal of the Ceramic Society of Japan. 105:703-706
Unidirectional carbon fiber-reinforced SiC/C composites were fabricated by the reaction bonding method with phenolic resin and silicon powder at 1450°C. Increasing of the Si/C ratio of the matrix from 0 to 1, the bulk density decreased from 1.84 to
Publikováno v:
Philosophical Magazine A. 74:957-964
Inhomogeneous deformation of a polycrystal due to grain-boundary sliding was studied geometrically. It was shown that deformation modes such as grain-boundary sliding and separation (diffusional migration) tend to localize owing to inherent inhomogen
Publikováno v:
Journal of the American Ceramic Society. 82:1355-1357
Plane-woven-fabric carbon-fiber-reinforced SiC/C matrix composites were fabricated at 1450°C via reaction bonding and impregnation with phenolic resin. The relationship between the flexural strength and the open porosity of the composites is depende
Publikováno v:
Journal of the American Ceramic Society. 82:2276-2278
Molybdenum carbosilicide composites (SiC-Mo ≤5 Si 3 C ≤1 ) were fabricated via the melt-infiltration process. The fracture behavior of the composites was studied from room temperature up to 1800°C in 1 atm (∼10 5 Pa) of argon. The bend strengt