V.S. Zakhvalinskii, E.A. Piliuk, S.V. Taran, A. Sklyarova, V.V. Matveev, J. Lindén, I. Zakharchuk
Publikováno v:
Results in Physics, Vol 6, Iss , Pp 1175-1177 (2016)
A La0.7Ca0.3Mn0.5Fe0.5O3 (LCMFO) ceramic sample was produced using conventional solid-state reactions. According to the X-ray diffraction data, the obtained sample has an orthorhombic space group Pnma (a = 5.482(2) Å, b = 7.739(3) Å, c = 5.446(3)
Externí odkaz:
https://doaj.org/article/742d7a16587f47e7a26e9b66b4b93274
Autor:
V.S. Zakhvalinskii, E.A. Piliuk, I. Yu Goncharov, A.V. Simashkevich, D.A. Sherban, L.I. Bruc, N.N. Curmei, M.I. Rusu, G.V. Rodrigez
Publikováno v:
Results in Physics, Vol 6, Iss , Pp 39-40 (2016)
Thin films of Si3N4 were prepared by non-reactive magnetron sputtering in an Ar atmosphere. A previously synthesized Si3N4 was used as a solid-state target. Deposition was carried out on a cold substrate of p-Si (100) with a resistivity of 2 Ohm cm.
Externí odkaz:
https://doaj.org/article/dd9e026ae1fb48fa82c2436697fc45d8
Autor:
E.A. Piliuk, S. V. Taran, V. S. Zakhvalinskii, Thi Thao Pham, Thi Tham Hong Nguyen, N. T. Dang
Publikováno v:
Journal of Electronic Materials. 46:3523-3530
A precursor powder was obtained from drying the solutions of a mixture of different ratios of Cu, Zn and Sn chloride and thiourea. The Cu2ZnSnS4 (CZTS) samples were prepared from thermal decomposition of the corresponding precursors in vacuum, and we
Autor:
I. Zakharchuk, Vladimir V. Matveev, V. S. Zakhvalinskii, S.V. Taran, Johan Lindén, Anastasia Sklyarova, E.A. Piliuk
Publikováno v:
Results in Physics, Vol 6, Iss, Pp 1175-1177 (2016)
A La0.7Ca0.3Mn0.5Fe0.5O3 (LCMFO) ceramic sample was produced using conventional solid-state reactions. According to the X-ray diffraction data, the obtained sample has an orthorhombic space group Pnma (a = 5.482(2) Å, b = 7.739(3) Å, c = 5.446(3)
Autor:
I. Goncharov, L. Bruc, A. V. Simashkevich, V. S. Zakhvalinskii, Marin Rusu, D.A. Sherban, N. Curmei, E.A. Piliuk
Publikováno v:
physica status solidi (a). 212:184-188
Thin films of predominantly amorphous n-type SiC were prepared by non-reactive magnetron sputtering in an Ar atmosphere. A previously synthesized SiC was used as a solid-state target. Deposition was carried out on a cold substrate of p-type Si (100)
Akademický článek
Tento výsledek nelze pro nepřihlášené uživatele zobrazit.
K zobrazení výsledku je třeba se přihlásit.
K zobrazení výsledku je třeba se přihlásit.
Akademický článek
Tento výsledek nelze pro nepřihlášené uživatele zobrazit.
K zobrazení výsledku je třeba se přihlásit.
K zobrazení výsledku je třeba se přihlásit.
Akademický článek
Tento výsledek nelze pro nepřihlášené uživatele zobrazit.
K zobrazení výsledku je třeba se přihlásit.
K zobrazení výsledku je třeba se přihlásit.