Jing-kun Li, Bin-guo Fu, Tian-shun Dong, Guo-lu Li, Wen-qing Sheng, Yong-yue Liu, Jia-geng Liu
Publikováno v:
Journal of Materials Research and Technology, Vol 24, Iss , Pp 6238-6245 (2023)
The effect of cold rolling reduction on the precipitation of σ phase at 800 °C in the 2906 DSS was investigated. The results show that the precipitation rate of the σ phase is improved with the increase of rolling reduction, and the maximum volume
Externí odkaz:
https://doaj.org/article/cd0aa76f0cf449fb9e02b0fbbff96ff8
Publikováno v:
Journal of Materials Research and Technology, Vol 18, Iss , Pp 448-460 (2022)
The effect of annealing temperature on the microstructure, mechanical property and anti-corrosion behavior of the X2CrNi12 ferritic stainless steel were systematically investigated. The results demonstrate that a large amount of (Fe, Cr)23C6 precipit
Externí odkaz:
https://doaj.org/article/4c557622c8cb4661b6ebd2d6f721a202
Publikováno v:
China Foundry, Vol 18, Iss 3, Pp 217-222 (2021)
In this work, a new (Y, Gd)H2 precipitate was identified and systematically investigated in the as-cast Mg-6Gd-3Y-0.5Zr alloy by XRD, SEM with EDS, TEM with EDS techniques and thermodynamics analysis. Results show that the as-cast alloy contains α-M
Externí odkaz:
https://doaj.org/article/4823cec1be4340289fbc75d1b5f4cc4d
Publikováno v:
China Foundry, Vol 17, Iss 6, Pp 455-463 (2020)
The microstructure and dry sliding wear performance of as-cast TiCp/Ti-1100-0.5Nb composite at 25 °C, 500 °C and 600 °C were systematically investigated. Results show that the solidification matrix microstructure is the typical Widmanstätten stru
Externí odkaz:
https://doaj.org/article/11e2fecd192949a5878d3e8bd8c276e1
Publikováno v:
China Foundry, Vol 15, Iss 3, Pp 173-181 (2018)
The effects of austempering temperature on microstructure and surface residual stress of carbidic austempered ductile iron (CADI) grinding balls were systematically investigated in this work. The microstructures were oberserved by optical metallograp
Externí odkaz:
https://doaj.org/article/f4d72f7761294fe68a32322326172a22
Publikováno v:
China Foundry, Vol 15, Iss 2, Pp 132-138 (2018)
In order to improve the corrosion resistance of magnesium lithium alloy, Mg-14Li alloy with different content of Ca (0, 3, 5, 10wt.%) was prepared with a induction melting furnace. Electrochemical test and corrosion test were carried out in NaCl solu
Externí odkaz:
https://doaj.org/article/d69daeeec2604677bd85f5a9728ffabe
Publikováno v:
China Foundry, Vol 13, Iss 5, Pp 346-351 (2016)
The formation mechanism of the spheroidal carbide in the ultra-low carbon ductile cast iron fabricated by the metal mold casting technique was systematically investigated. The results demonstrated that the spheroidal carbide belonged to eutectic carb
Externí odkaz:
https://doaj.org/article/1c3177d7e2c0490f899a5ba20a10865f
Autor:
Fei Wang1,2 wangyufeng_412@163.com, Bin-guo Fu1,3 fubinguohao@163.com, Yu-feng Wang3, Tian-shun Dong1, Guo-lu Li1, Jin-hai Liu1
Publikováno v:
China Foundry. Sep2024, Vol. 21 Issue 5, p599-612. 14p.
Publikováno v:
In Surface & Coatings Technology 25 August 2019 372:451-462
Autor:
Guo-lu, Li, Ya-long, Li, Tian-shun, Dong, Bin-Guo, Fu, Hai-dou, Wang, Xiao-dong, Zheng, Xiu-kai, Zhou
Publikováno v:
In Vacuum October 2018 156:440-448