Autor:
T, Divya Sherin G, Bhowmik, R. N
We report the doping high concentration of tetravalent Ge4+ ions (5 mol % for x = 0.05 to 30 mol % for x = 0.30) at the Fe3+ sites of Fe2-xGexO3 system by chemical coprecipitation route. The charge state of Fe and Ge ions has been modified into lower
Externí odkaz:
http://arxiv.org/abs/2309.03634
Publikováno v:
Sup. Sci. Tech. (2022)
A perfect topological superconductor can be realized by the simultaneous existence of bulk superconductivity along with topological non-trivial surface states. In this article, we report single crystal growth of superconducting binary compound Pb2Pd.
Externí odkaz:
http://arxiv.org/abs/2112.07276
The low temperature lattice structure and magnetic properties of Co$_{2.75}$Fe$_{0.25}$O$_4$ ferrite have been investigated using experimental results from synchrotron x-ray diffraction (SXRD), dc magnetization, ac susceptibility, neutron diffraction
Externí odkaz:
http://arxiv.org/abs/2007.03906
Akademický článek
Tento výsledek nelze pro nepřihlášené uživatele zobrazit.
K zobrazení výsledku je třeba se přihlásit.
K zobrazení výsledku je třeba se přihlásit.
Akademický článek
Tento výsledek nelze pro nepřihlášené uživatele zobrazit.
K zobrazení výsledku je třeba se přihlásit.
K zobrazení výsledku je třeba se přihlásit.
Autor:
Bhowmik, R. N., Ranganathan, R.
A comparative study of the non-equilibrium magnetic phenomena (magnetic blocking, memory, exchange bias and aging effect) has been presented for ferrimagnetic Co$_{1.75}$Fe$_{1.25}$O$_4$ (CFO) and its composite with non-magnetic BaTiO$_3$ (BTO). Sync
Externí odkaz:
http://arxiv.org/abs/2001.02602
Alpha-Fe2O3 and alpha-Cr2O3 has been mechanical alloyed to prepare Fe1-xCrxO3 oxides for x = 0.2-0.8. Synchrotron X-ray diffraction and Raman spectra have shown inhomogeneous structure of {\alpha}-Fe2O3 and {\alpha}-Cr2O3 phases in as-alloyed samples
Externí odkaz:
http://arxiv.org/abs/2001.02831
We report high temperature synchrotron X-ray diffraction (SXRD), dc magnetization and current-voltage (I-V) characteristics for the samples of Co$_{2.75}$Fe$_{0.25}$O$_4$ ferrite. The material was prepared by chemical reaction of the Fe and Co nitrat
Externí odkaz:
http://arxiv.org/abs/2001.02829
Autor:
Mondal, Binita, Dan, Shovan, Mondal, Sudipta, Bhowmik, R. N., Ranganathan, R., Mazumdar, Chandan
The binary compounds GdIr3, TbIr3 and HoIr3 are synthesized successfully and found to form in macroscopic co-existence of two polymorphic phases: C15b and AuCu3-type. The dc magnetization and heat capacity studies confirm that C15b phase orders ferro
Externí odkaz:
http://arxiv.org/abs/1904.04807