Publikováno v:
Refractories. 32:479-482
A composition of mullite-corundum ramming compound has been developed with production of an experimental lot at Semiluki Refractory Plant. This compound was used to line the tuyere assemblies of No. 2 Blast Furnace of Kosogorsk Metallurgical Plant, w
Publikováno v:
Refractories. 27:549-555
Etude du comportement des garnissages de haut fourneau dans une atmosphere basique. Caracterisation par spectrometrie IR des refractaires soumis aux vapeurs alcalines
Publikováno v:
Refractories. 17:478-486
A comprehensive comparative analysis of the principal properties of the refractories used for the lining of blast furnaces showed that the ShKD-type kaolin refractories produced by the Zaporozhe Refractories Plant possess the highest property indices
Autor:
Z. D. Zhukova, V. I. Bondarenko, V. Ya. Tolstaya, V. P. Safronova, V. A. Shatlov, N. V. Gul'ko, L. E. Azarenkova, B. N. Starshinov
Publikováno v:
Refractories. 18:209-216
The refractory lining of the cooled part of the stack eroded before the end of the campaign and the blast furnace was operated for 18 months without this masonry.
Autor:
N. A. Voronova, S. T. Pliskanovskii, G. A. Shtein, N. N. Popova, Yu. V. Vyazovskii, B. N. Starshinov, E. N. Vishnyakova, O. A. Mogilevtsev
Publikováno v:
Metallurgist. 18:20-23
Publikováno v:
Metallurgist. 19:248-252
Autor:
T. P. Khmelenko, N. V. Pitak, Z. D. Zhukova, B. N. Starshinov, N. V. Gul'ko, R. S. Shulyak, R. M. Fedoruk
Publikováno v:
Refractories. 18:722-728
The investigation showed that the resistance to the action of blast-furnace slag and cast iron is highest for blocks of fused Bakor, sintered kaolin refractories, and fused kaolin. The interaction of the refractories with cast iron causes the surface
Autor:
R. E. Shcherbina, B. N. Starshinov, V. Ka. Zima, R. M. Fedoruk, G. A. Belokrys, T. P. Khmelenko, R. S. Shulyak, I. P. Davydov, N. V. Pitak
Publikováno v:
Refractories. 17:404-410
The formation of the black core in large kaolin bricks during the firing process is caused mainly by the reducing medium which develops in the central part of these high-density refractories, graphitizes the carbon, and converts some of the high-vale
Autor:
K. E. Kapran, N. V. Pitak, I. P. Konnov, L. A. Dikun, B. N. Starshinov, N. P. Ivanov, L. V. Medvedev, V. A. Khreshchenyuk, M. D. Dubovaya, T. P. Khmelenko, A. P. Bakalkin, R. M. Fedoruk
Publikováno v:
Refractories. 20:271-276
The Ukrainian Institute of Refractories has developed a technology, and the Chasov-Yar Factory is mastering the manufacturing methods, for dense kaolin refractories with a porosity of not more than 12% for blast furnaces. The bricks are made with hig
Publikováno v:
Metallurgist. 22:458-461