Zobrazeno 1 - 8
of 8
pro vyhledávání: '"A.E.A. Chemin"'
Autor:
Carla Isabel dos Santos Maciel, Waldek Wladimir Bose Filho, Fernando Antonio Pascoal, Cassius Olívio Figueiredo Terra Ruchert, Conrado Ramos Moreira Afonso, A.E.A. Chemin
Publikováno v:
Repositório Institucional da USP (Biblioteca Digital da Produção Intelectual)
Universidade de São Paulo (USP)
instacron:USP
Universidade de São Paulo (USP)
instacron:USP
Externí odkaz:
https://explore.openaire.eu/search/publication?articleId=doi_dedup___::8942ab600b58f5c56352d3f770a2998a
https://doi.org/10.1002/mdp2.79
https://doi.org/10.1002/mdp2.79
Publikováno v:
Engineering Failure Analysis. 108:104286
The main aim of this study is investigating the possible failures classified as subcase origin fatigue and further case crushing. Because of these failure mechanisms, the teeth of the intermediate gears shaft may fracture after several cycles of oper
Externí odkaz:
https://explore.openaire.eu/search/publication?articleId=doi_________::24227ef4cd95a982ccda881ae60110e0
https://doi.org/10.1016/j.engfailanal.2019.104286
https://doi.org/10.1016/j.engfailanal.2019.104286
Publikováno v:
Procedia Engineering. 101:85-92
Corrosion crack propagation experiments were carried out on specimens of 7475 T7351 aluminum alloy. Variable amplitude tests were performed with flight-simulated spectrum Twist ( Transport Aircraft Wing Structures ) and Falstaff ( Fighter Aircraft Lo
Externí odkaz:
https://explore.openaire.eu/search/publication?articleId=doi_dedup___::22775ee5e69304ab04cf2db7dbf33f8c
Autor:
Dirceu Spinelli, F. Saconi, W.W. Bose Filho, A.E.A. Chemin, Cassius Olívio Figueiredo Terra Ruchert
Publikováno v:
Repositório Institucional da USP (Biblioteca Digital da Produção Intelectual)
Universidade de São Paulo (USP)
instacron:USP
Universidade de São Paulo (USP)
instacron:USP
The corrosion fatigue crack propagation was studied on the 7475 T7351 aluminum alloy under a standardized load sequence for flight simulation tests on transport aircraft wing structures (TWIST) simulated loading under a mean stress 80 MPa. The corros
Externí odkaz:
https://explore.openaire.eu/search/publication?articleId=doi_dedup___::de7def787d3f45d60a3334ae522b7f4f
Autor:
Leandro Duarte Bisanha, Cassius Olívio Figueiredo Terra Ruchert, Artur de Jesus Motheo, Waldek Wladimir Bose Filho, A.E.A. Chemin, Denys Marques
Publikováno v:
Repositório Institucional da USP (Biblioteca Digital da Produção Intelectual)
Universidade de São Paulo (USP)
instacron:USP
Universidade de São Paulo (USP)
instacron:USP
The development of aluminum alloys of the Al–Zn–Mg–Cu system is the primary factor that enabled the evolution of aircraft. However, it has been shown that these alloys tend to undergo pitting corrosion due to the presence of elements such as ir
Externí odkaz:
https://explore.openaire.eu/search/publication?articleId=doi_dedup___::89161d2e7449355f96d5c82960018c09
Akademický článek
Tento výsledek nelze pro nepřihlášené uživatele zobrazit.
K zobrazení výsledku je třeba se přihlásit.
K zobrazení výsledku je třeba se přihlásit.
Akademický článek
Tento výsledek nelze pro nepřihlášené uživatele zobrazit.
K zobrazení výsledku je třeba se přihlásit.
K zobrazení výsledku je třeba se přihlásit.
Akademický článek
Tento výsledek nelze pro nepřihlášené uživatele zobrazit.
K zobrazení výsledku je třeba se přihlásit.
K zobrazení výsledku je třeba se přihlásit.