Ana Cuesta, Ángeles G. De la Torre, Isabel Santacruz, Ana Diaz, Pavel Trtik, Mirko Holler, Barbara Lothenbach, Miguel A. G. Aranda
Publikováno v:
IUCrJ, Vol 6, Iss 3, Pp 473-491 (2019)
Mortars and concretes are ubiquitous materials with very complex hierarchical microstructures. To fully understand their main properties and to decrease their CO2 footprint, a sound description of their spatially resolved mineralogy is necessary. Dev
Externí odkaz:
https://doaj.org/article/f90ad6784a744a949cb060e146043668
Autor:
K. Morsli, Ángeles G. de la Torre, Antonio J. M. Cuberos, Mohammed Zahir, Miguel A. G. Aranda
Publikováno v:
Materiales de Construccion, Vol 59, Iss 294, Pp 19-29 (2009)
Activated white cement clinkers with a theoretical 60% (wt) belite (dicalcium silicate) content were prepared at a temperature 100 ºC lower than used to manufacture conventional white Portland cement clinkers. Activation was achieved by adding varia
Externí odkaz:
https://doaj.org/article/792eda6b74c64ce781e14faf20dc1014
Autor:
J. Manuel Porras-Vázquez, Ángeles G. De la Torre, David Marrero-López, Enrique R. Losilla, Miguel A. G. Aranda
Publikováno v:
Dalton Transactions: An International Journal of Inorganic Chemistry; May2006, Vol. 2006 Issue 22, p2691-2697, 7p
Publikováno v:
Crystals, Vol 8, Iss 3, p 110 (2018)
The Rietveld-internal standard method for Bragg-Brentano reflection geometry (θ/2θ) X-ray diffraction (XRD) patterns is implemented to determine the amorphous phase content. The effect of some minor phases on quantitative accuracy is assessed. The
Externí odkaz:
https://doaj.org/article/ea18c104b5a04d218fa00762f3dbf5c9
Autor:
Ana Cuesta, Jesus D. Zea-Garcia, Diana Londono-Zuluaga, Angeles G. De la Torre, Isabel Santacruz, Oriol Vallcorba, Miguel A.G. Aranda
Publikováno v:
Crystals, Vol 7, Iss 10, p 317 (2017)
The analysis of atomic ordering in a nanocrystalline phase with small particle sizes, below 5 nm, is intrinsically complicated because of the lack of long-range order. Furthermore, the presence of additional crystalline phase(s) may exacerbate the pr
Externí odkaz:
https://doaj.org/article/b9574f84787a4dd383fbddc6cbc24908