Tie Liu, Yusong Suo, Ruixue Zhang, Jianzhong Cui, Congfu Liu, Lei Li, Lin Yang, Huanzheng Jiao
Publikováno v:
Journal of Materials Science & Technology. 103:244-260
In this work, Zn microalloyed with Al, Mn, Cu, Ag and Li was cast, annealed and extruded. The results showed that addition of multiple trace elements causes significant change in the microstructures, mechanical properties and corrosion behavior of Zn
Publikováno v:
Inorganic Chemistry Frontiers. 9:249-258
The electrocatalytic activity of nanoalloy catalysts could be effectively manipulated by tuning their intrinsic physical and chemical properties (e.g., compositions, facets, lattice strain, morphologies, etc.). However, it still remains a challenge h
Publikováno v:
Ceramics International. 47:31907-31914
All-solid-state batteries have recently attracted much attention for their high energy density and safety. Li2ZrO3-based Li-ion conductors with high electrochemical stability have potential applications for electrolytes in all-solid-state batteries.
Autor:
Kai Chen, Jingjiu Yuan, Haichao Gong, Zhiming Zhou, Duoduo Wang, Xingwang Cheng, Qunbo Fan, Xinjie Zhu, Lin Yang
Publikováno v:
Journal of Materials Research and Technology, Vol 15, Iss, Pp 3099-3109 (2021)
The important but highly complex α/β Burgers orientation relationship and slip behavior of a Ti–5.5Mo–7.2Al–4.5Zr–2.6Sn–2.1Cr titanium alloy plate were obtained and elaborated, which was subjected to hot rolling with 20%, 40%, and 60% red
Publikováno v:
MATERIALS TRANSACTIONS. 62:1609-1613
Publikováno v:
Metals and Materials International. 28:448-455
A new lightweight, refractory high entropy alloy (HEA), CrNbTa0.25TiZr, was prepared by arc-melting under a vacuum condition. The as-cast and annealed CrNbTa0.25TiZr possessed identical dual-phase components: a BCC + a cubic Laves phase. After anneal
Publikováno v:
Transactions of the Indian Institute of Metals. 75:79-90
A series of Al-xZn alloys (x = 0–30 wt.%) were prepared to investigate the effect of Zn on their structure and mechanical properties. The alloys with Zn content ranging from 0 to 10 wt.% were consisted of single α-Al solid solution phases, but whe
Autor:
Zhi-min Guo, Yuan-long Wang, Xiao-lin Yang, Bin Liu, Ji-xian Zhang, Da-shan Sui, Chang-zeng Luo, Guang-hong Hu
Publikováno v:
China Foundry. 18:497-504
Publikováno v:
Physics of Metals and Metallography. 122:1342-1349
A novel 3d transition metal high-entropy alloy (3d TM HEA), Al0.5CoCrCuV, was designed through the substitution of Fe and Ni by V in the base alloy Al0.5CoCrCuFeNi, and then was fabricated by arc-melting. The phase components of the studied alloy in
Publikováno v:
Physics of Metals and Metallography. 122:1500-1506
A new refractory alloy, CrHfNbZrTa0.5, was prepared by a vacuum arc-melting, and its phase analysis, microstructures, and compressive properties in as-cast and annealed conditions were investigated. The phase components of the as-cast CrHfNbZrTa0.5 a