Zobrazeno 1 - 10
of 355
pro vyhledávání: '"02"'
Publikováno v:
Corrosion. 77:906-922
Cold-drawn, high-strength, prestressing (PS) steel strands are widely used in pretensioned concrete (PTC) structures. This paper discusses the stress corrosion cracking (SCC) of PS steel embedded in cement mortar and gradually exposed to chlorides. V
Autor:
Jiarong Ma, Zhanpeng Lu, Yibo Jia, Junjie Chen, Shuangliang Yang, Qi Xiong, Kun Zhang, Tongming Cui, Zhimin Zhong, Sergio Lozano-Perez, Tetsuo Shoji, Hui Zheng
Publikováno v:
Corrosion. 77:878-895
Exposure and slow strain rate tensile tests were conducted in a simulated pressurized water reactor (PWR) primary water to investigate the oxidation resistance and stress corrosion cracking (SCC) susceptibility of 308L and 309L stainless steel (SS) c
Publikováno v:
Corrosion. 77:681-692
Corrosion under insulation (CUI) is among the key concerns for the integrity of process equipment and pipelines. Various measures to detect and fix the damages from CUI pose significant maintenance expenditures in hydrocarbons processing facilities.
Publikováno v:
Corrosion. 77:370-375
In CORROSION’S June 2020 editorial,1 we explored the COVID-192 pandemic and the antimicrobial function of copper and silver enabled by corrosion Since that editorial was written, we have gone from 2 1 million confirmed infections and over 143,000 r
Publikováno v:
Corrosion. 77:655-667
In this paper, the corrosion behavior of three kinds of medium Cr low C steels in the simulated service environment of the transport pipeline was investigated through accelerated corrosion experiments, and the corrosion resistance mechanism of these
Publikováno v:
Corrosion. 77:593-599
This paper will report on a new membrane-based electrochemical sensor that may provide an important utility in monitoring and characterizing internal corrosion of natural gas pipelines. Using this sensor, the corrosion rate of X65 steel exposed to H2
Autor:
Harvey M. Thompson, José Antônio da Cunha Ponciano Gomes, M. Al-Khateeb, Anne Neville, Mariana Costa Folena, K.A. Mohammed, S.S. de Carvalho, Richard Barker
Publikováno v:
Corrosion. 77:515-525
This paper presents an experimental and theoretical investigation into water condensation and corrosion under noncorrosion product forming conditions at the top of the line in a static, CO2 environment. An experimental test cell is developed to measu
Autor:
Carol Glover, G. L. Mantovani, Juliana Sarango de Souza, Maina Portella Garcia, Ramachandran Vasant Kumar, Renato Altobelli Antunes, Geraint Williams, Phil Ansell
Publikováno v:
Corrosion. 77:564-576
Global and local corrosion techniques were used to study the corrosion behavior of weld joints of a high-strength low-alloy steel (LNE500) typically used in the automotive industry in Brazil. The welded joints were prepared by gas metal arc welding.
Publikováno v:
Corrosion. 77:646-654
Corrosion mitigation is an important aspect of amine-based post-combustion carbon dioxide (CO2) capture operations due to the desire to use less expensive but corrosion-vulnerable materials such as low carbon steels in the construction of a capture s
Autor:
D.W. Shoesmith, Mark C. Biesinger, S. Ramamurthy, Jeffrey D. Henderson, G.B. McGarvey, Fraser P. Filice, James J. Noël
Publikováno v:
Corrosion. 77:540-551
The ability of fluoride ions, in trace concentrations, to promote film instability and transpassive dissolution was shown for several corrosion-resistant alloys. While the addition of fluoride ion was found to decrease the transpassive dissolution po