Corrosion. 79:333-350
Environmentally assisted cracking of various high-strength nickel-based alloys used for subsea components was studied from the perspective of fatigue crack growth rate (FCGR) and static crack growth rate (SCGR) as a function of several critical varia
Publikováno v:
Corrosion. 78:963-981
Aging pipeline infrastructure is subject to various degradation modes, in particular, there is a growing concern about stress corrosion cracking (SCC) from external environments. The current program focused on developing data in high pH carbonate/bic