Yuhei Ogawa, Yusuke Funakoshi, Saburo Matsuoka, Koichi Okita, Osamu Takakuwa, Hisao Matsunaga, Saburo Okazaki
Publikováno v:
Corrosion Science. 161:1-17
形態: カラー図版あり
Physical characteristics: Original contains color illustrations
Accepted: 2019-08-26
資料番号: PA2010049000
Physical characteristics: Original contains color illustrations
Accepted: 2019-08-26
資料番号: PA2010049000
Publikováno v:
Que, Z, Seifert, H P, Spätig, P, Zhang, A, Holzer, J, Rao, G S & Ritter, S 2019, ' Effect of dynamic strain ageing on environmental degradation of fracture resistance of low-alloy RPV steels in high-temperature water environments ', Corrosion Science, vol. 152, pp. 172-189 . https://doi.org/10.1016/j.corsci.2019.03.013
Elastic plastic fracture mechanics tests on different low-alloy reactor pressure vessel (RPV) steels in air and various simulated light water reactor environments revealed a clear, but moderate reduction of the fracture initiation resistance of RPV s
Autor:
Hisao Matsunaga, Saburo Okazaki, Osamu Takakuwa, Saburo Matsuoka, Yuhei Ogawa, Yusuke Funakoshi
Publikováno v:
Corrosion Science. 174
Accepted: 2020-06-11
資料番号: PA2110038000
資料番号: PA2110038000
Autor:
Hang Su, Akihisa Takeuchi, Ryohei Masunaga, Dongsheng Fu, Kyosuke Hirayama, Hiroyuki Toda, Kazuyuki Shimizu, Masayuki Uesugi
Publikováno v:
Corrosion Science. 184:109343
Al-10Mg alloys, which are highly susceptible to SCC, were prepared with various β precipitate morphologies. Interrupted in-situ tensile tests were conducted under synchrotron X-ray radiation, employing a recently developed X-ray microtomography tech
Publikováno v:
Corrosion Science
Corrosion Science, Elsevier, 2019, 150, pp.1-8. ⟨10.1016/j.corsci.2019.01.003⟩
Corrosion Science, Elsevier, 2019, 150, pp.1-8. ⟨10.1016/j.corsci.2019.01.003⟩
International audience; Three kinds of Pt-rich γ-γ’ bond-coating were processed with different contents in Pt and Al. The cyclic oxidation tests performed at 1100 °C on TBC systems showed the superiority of the Pt-rich γ-γ’ coatings when com
Publikováno v:
Corrosion Science.
Cyclic and isothermal oxidation behaviors of first and fourth-generation superalloys AM1 and MCNG were investigated to evaluate the ability of the scratch test to quantify the adhesion of multi-layered oxide scales. Effects of sulfur content and of s