CORROSION. 27:55-62
An extended feasibility study was made of the use of the metalliding process to the application of highly impervious diffusion coatings on inexpensive conductive metals which normally corrode in acid electrolytes. Tantalum and hafnium, which proved h
Autor:
Mary Boehm Strauss, M. C. Bloom
Publikováno v:
CORROSION. 16:553t-556t
Aqueous corrosion of mild steel at 316 G is greatly accelerated by low concentrations of FeCl3. This can lead to stress corrosion cracking in plastically deformed areas subject to high str...
Publikováno v:
CORROSION. 19:247t-253t
A study was made of the effect of applied stress on the stress corrosion crack morphology resulting from the exposure of Types 304, 309 and 316 austenitic stainless steel wire specimens to...
Autor:
J. E. Prior
Publikováno v:
Corrosion. 15:17-17
Failure occurred in a Type 316 stainless steel valve seat ring after nine months' service in a water treating system. Visual examination showed the ring had suffered intergranular corrosion after exposure to dilute sulfuric acid. The ring also had a