Publikováno v:
Corrosion. 71:771-783
A test assembly consisting of a coated and scribed aluminum alloy 7075-T6 panel galvanically connected to uncoated through-hole noble fasteners has recently been utilized to quantify corrosion attack during corrosion testing in laboratory chambers. I
Autor:
Gerald S. Frankel, B.C. Rincon Troconis, Longfei Li, W.C. Nickerson, C.A. Matzdorf, R.G. Buchheit
Publikováno v:
Corrosion. 69:1240-1246
A test sample incorporating a coated and scribed Al alloy panel and uncoated through-hole fasteners was designed to provide accelerated response during atmospheric corrosion testing in the field or in laboratory chambers. Protective coatings that wou
Publikováno v:
CORROSION. 63:1114-1123
The rate of stress corrosion cracking (SCC) was measured for nonsensitized, cold-worked Type 316 (UNS S31600) and Type 304 (UNS S30400) in both hydrogenated pressurized water reactor (PWR)...
Publikováno v:
CORROSION. 62:44-53
During fusion welding of stainless steels and other high-Cr alloys, evaporation and oxidation of Cr from the molten weld pool result in the generation of carcinogenic hexavalent chromium (Cr[VI]) in the welding fume. Stringent new exposure limits fro
Publikováno v:
CORROSION. 61:219-229
The primary water stress corrosion cracking (PWSCC) of Alloy 600 (UNS N06600), Type 304 (UNS S30400), and Type 316 (UNS S31600) stainless steels (SS) was studied at 360°C and at nominal st...
Autor:
Rokuro Nishimura, Yasuaki Maeda
Publikováno v:
CORROSION. 60:650-657
The stress corrosion cracking (SCC) behavior of the commercial austenitic stainless steels, Type 304 and Type 316 (UNS S30400 and UNS S31600), has been investigated in acidic solutions to ...
Publikováno v:
CORROSION. 58:57-71
The corrosion and galvanic compatibility of a high-strength copper-nickel alloy, MARINEL, to martensitic (Type 416 S21 [UNS S41600]) and general-purpose austenitic (Type 316 S11 [UNS S31600]) stainless steels (SS) were investigated in natural seawate
Autor:
P. J. Dudt, A. J. Sedriks
Publikováno v:
CORROSION. 57:84-91
This article reviews the issues relating to corrosion behavior, coating technology, and magnetic properties of certain austenitic stainless steels being considered as candidate materials for the nonmagnetic advanced double hulls of future U.S. Navy c
Publikováno v:
CORROSION. 56:289-297
The sensitization resistance of the stabilized Type 347 (UNS S34700) stainless steels (SS) having different carbon and nitrogen contents was evaluated using the double-loop electrochemical potentiokinetic reactivation (DL-EPR) and ASTM A262, practice
Publikováno v:
CORROSION. 55:128-138
The electrochemical, galvanic, and mechanical responses of grade 2 titanium in 6% sodium chloride (NaCl) solution at different temperatures were investigated. The initial corrosion potential and cathodic reaction rate increased with decreasing pH and