Autor:
B. E. Wilde, M. C. Juhas
Publikováno v:
CORROSION. 46:812-822
Type 316 (UNS S31600) stainless steel (SS) is a candidate alloy for containment of high-level nuclear waste in deep underground storage. The heat-affected zones (HAZs) of welded containers could become sensitized under the appropriate thermal conditi
Publikováno v:
CORROSION. 71:1027-1035
The primary water stress corrosion cracking (PWSCC) susceptibility of Ni-based alloys, such as Alloy 600 (UNS N06600), has been much higher than that of Fe-based alloys, such as Type 316 stainless steel (UNS S31600). This phenomenon is generally reco
Publikováno v:
CORROSION. 63:1114-1123
The rate of stress corrosion cracking (SCC) was measured for nonsensitized, cold-worked Type 316 (UNS S31600) and Type 304 (UNS S30400) in both hydrogenated pressurized water reactor (PWR)...
Publikováno v:
CORROSION. 62:44-53
During fusion welding of stainless steels and other high-Cr alloys, evaporation and oxidation of Cr from the molten weld pool result in the generation of carcinogenic hexavalent chromium (Cr[VI]) in the welding fume. Stringent new exposure limits fro
Publikováno v:
CORROSION. 56:289-297
The sensitization resistance of the stabilized Type 347 (UNS S34700) stainless steels (SS) having different carbon and nitrogen contents was evaluated using the double-loop electrochemical potentiokinetic reactivation (DL-EPR) and ASTM A262, practice
Publikováno v:
CORROSION. 44:328-333
Direct measurements of grain boundary chromium depletion by energy dispersive x-ray spectroscopy (EDS) in a scanning transmission electron microscope (STEM) are compared to measurements of the degree of sensitization (DOS) using the electrochemical p
Autor:
A. McMinn, Richard A. Page
Publikováno v:
Corrosion. 44:239-247
The stress corrosion cracking (SCC) susceptibilities of Alloys 600 and 690, AISI 316 NG stainless steel (SS), ASTM A508 carbon steel, and a number of compatible weld metals have been evaluated at 288 C in pure water and in pure water containing sulfu
Publikováno v:
Corrosion. 25:194-198
Corrosion tests were run for periods up to 5000 hrs in borated water at 600 F (316 C) in a high velocity loop on strip, tubes, and weldments of Alloy 600. During the first 1000 to 2000 hrs of exposure, corrosion rate differences depending upon surfac