CORROSION. 71:57-64
Under pressurized water reactor primary conditions, the stress corrosion cracking susceptibility of Alloy 600 (UNS N06600) is improved by chromium carbide precipitation in the grain boundaries. However, the effect of chromium depletion on stress corr
Publikováno v:
CORROSION. 70:1177-1180
Advanced metal waste-form alloys (60SS[316]-12Zr-12Mo) are comprised of a multi-phase microstructure and display rather complex corrosion behavior. To understand this behavior, a combination of electrochemical techniques, microscopic analyses, microe
Publikováno v:
CORROSION. 65:748-757
Corrosion resistance of AISI 316 (UNS S31600) exposed to lithium bromide (LiBr) solution (50 wt%) was investigated using the electrochemical noise (EN), polarization curves (PC), and the weight-loss method (WL) at 25, 50, 60, 70, and 80°C. The goal
Publikováno v:
Scopus-Elsevier
The corrosion resistance of Type 316 (UNS S31600) austenitic stainless steel in an aggressive environment containing Cl− ions in the as-received state and after nanostructuralization caused by severe plastic deformation by hydrostatic extrusion (HE
Publikováno v:
Corrosion. 68:784-792
Corrosion assessment of metal waste form (MWF) alloys was carried out in two possible geological repository environments, simulated Kalpakkam groundwater (KGW) and Rajasthan groundwater (RGW). The corrosion resistance properties, passive film stabili
Autor:
Naima Maouche, Belkacem Nessark
Publikováno v:
CORROSION. 64:315-324
Polyterthiophene (P3T) film was synthesized on Types 304 (UNS S30400) and 316 (UNS S31600) stainless steel (SS) electrodes from an acetonitrile (ACN) solution containing 10−2 M terthiophene (3T) and 10−1 M lithium perchlorate (LiClO4), by cycling
Publikováno v:
CORROSION. 63:1033-1041
A crack growth rate test on a compact tension specimen of Type 316 (UNS S31600) stainless steel was conducted in pure water under both subcritical and supercritical conditions. The crack g...
Autor:
S. Amancherla, T. Ramgopal
Publikováno v:
CORROSION. 61:1136-1144
This work is aimed at improving the understanding of the localized corrosion of stainless steel in methanolic solutions. Potentiodynamic polarization curves on Type 316 (UNS S31600) were measured in methanol (CH3OH)-water (H2O)-1 M lithium chloride (
Autor:
Yutaka Watanabe, Yoshiaki Kurata, Nishimura Kenji, Ryutaro Fujisawa, Motohiro Sakaihara, Takashi Nishida
Publikováno v:
CORROSION. 62:270-274
The objectives of this study were to evaluate the corrosion behavior of candidate corrosion-resistant alloys in slightly oxidizing or reducing supercritical water (SCW) environments contai...
Publikováno v:
CORROSION. 60:873-880
Round tensile specimens of AISI Type 316N (UNS S31651) stainless steel weld metal, made by manual metal arc welding (MMAW) process using heat inputs ranging from 3.07 kJ/cm to 7.41 kJ/cm, were subjected to stress corrosion cracking (SCC) tests in boi