Zobrazeno 1 - 8
of 8
pro vyhledávání: '"316"'
Publikováno v:
CORROSION. 70:1177-1180
Advanced metal waste-form alloys (60SS[316]-12Zr-12Mo) are comprised of a multi-phase microstructure and display rather complex corrosion behavior. To understand this behavior, a combination of electrochemical techniques, microscopic analyses, microe
Publikováno v:
Corrosion. 68:784-792
Corrosion assessment of metal waste form (MWF) alloys was carried out in two possible geological repository environments, simulated Kalpakkam groundwater (KGW) and Rajasthan groundwater (RGW). The corrosion resistance properties, passive film stabili
Publikováno v:
Corrosion. 41:720-727
The corrosion behavior of AISI 304 and 316 stainless steels (SSs) in hot concentrated caustic soda solutions was investigated under heat-transfer conditions. The corrosion potential of the specimens was located in the active region; thus, the alloys
Autor:
F. P. Mertens
Publikováno v:
Corrosion. 34:359-364
Reflectance infrared studies of the oxidation of Types 304, 316, and 410 stainless steels, in oxygen at various temperatures, are described. Similar studies, directed toward the interpretation of the stainless steel oxide reflectance spectra, are pre
Publikováno v:
CORROSION. 51:826-836
Superferritic stainless steels (SS) can suffer from dissimilar metal crevice (DMC) corrosion when part of a crevice with certain other stainless alloys. For example, UNS S44735 is attacked when part of a crevice with type 316 SS (UNS S31600) but not
Publikováno v:
CORROSION. 48:579-586
In this study, an attempt was made to investigate the pitting and intergranular corrosion susceptibility of as-deposited and thermally aged weldments of type 316LN stainless steel (SS) made by shielded metallic arc (SMA) welding process using 316 SS
Autor:
G. W. Beckman, Donald Warren
Publikováno v:
CORROSION. 13:33-48
The sulfide corrosion cracking behavior of Type 4140 bolts was studied in H2S-H2O systems at temperatures of 20 to 120 C and at pressures of 1 to 17 atmospheres. The susceptibility to cracking increased with increasing bolt hardness, increasing appli
Autor:
J. E. Prior
Publikováno v:
Corrosion. 15:17-17
Failure occurred in a Type 316 stainless steel valve seat ring after nine months' service in a water treating system. Visual examination showed the ring had suffered intergranular corrosion after exposure to dilute sulfuric acid. The ring also had a