Autor:
P. S. Maiya, W. J. Shack
Publikováno v:
Corrosion. 41:630-634
The relative stress corrosion cracking (SCC) susceptibility of heat-treated AISI 316 nuclear grade (NG) and 316 stainless steel (SS) has been investigated by means of constant extension rate tensile (CERT) tests over a range of strain rates from 10
Autor:
R. F. Hochman, M. Marek
Publikováno v:
CORROSION. 27:361-370
Crystallography, morphology, and kinetics of stress corrosion cracking (SCC) in austenitic stainless steels exposed to boiling, aqueous 45% magnesium chloride solution were studied on single crystal specimens of a Type 316 stainless steel. Notched sp
Publikováno v:
CORROSION. 46:641-652
Low-frequency fatigue tests at load ratios 0.8 and 0.9 and constant load tests were run on sensitized type 304 (UNS S30400) stainless steel (SS), type 316 nuclear grade (NG) SS and the nickel-base alloy 600 (UNS N06600) in simulated boiling water rea
Autor:
J. R. Cahoon, Y. R. Qian
Publikováno v:
CORROSION. 53:129-135
Corrosion fatigue tests on annealed type 316 (UNS S31600) stainless steel (SS) showed the maximum stress level for failure in 0.5 M sodium chloride (NaCl) aqueous solution at pH = 4.2 was ...
Autor:
Warren H. Bamford, David M. Moon
Publikováno v:
CORROSION. 36:289-298
The fatigue crack growth behavior of A533B and A508 pressure vessel steel and Types 304 and 316 steels used in reactor coolant piping has been studied in a pressurized water reactor environment at 288 C (550 F). The influence of stress ratio (Pmin/Pm