Publikováno v:
CORROSION. 71:57-64
Under pressurized water reactor primary conditions, the stress corrosion cracking susceptibility of Alloy 600 (UNS N06600) is improved by chromium carbide precipitation in the grain boundaries. However, the effect of chromium depletion on stress corr
Autor:
B. E. Wilde, M. C. Juhas
Publikováno v:
CORROSION. 46:812-822
Type 316 (UNS S31600) stainless steel (SS) is a candidate alloy for containment of high-level nuclear waste in deep underground storage. The heat-affected zones (HAZs) of welded containers could become sensitized under the appropriate thermal conditi
Publikováno v:
Corrosion. 74:5-23
Operando x-ray tomography was used to study the galvanic corrosion between aluminum alloy 7050-T7451 and Type 304 stainless steel using a simulated fastener covered with droplets of either 4 M NaCl or 2 M MgCl2. The simulated rivet was an x-ray trans
Autor:
Noelle Easter C. Co, James T. Burns
Publikováno v:
CORROSION. 72:1215-1219
Electrochemical experiments were used to create morphologies representative of galvanically-induced corrosion between aluminum alloy (AA) 7050-T7451 (UNS A97050) and Type 316 steel (UNS S31600) in a fastener configuration. The effects of these corros
Publikováno v:
CORROSION. 71:1027-1035
The primary water stress corrosion cracking (PWSCC) susceptibility of Ni-based alloys, such as Alloy 600 (UNS N06600), has been much higher than that of Fe-based alloys, such as Type 316 stainless steel (UNS S31600). This phenomenon is generally reco
Publikováno v:
Corrosion. 41:720-727
The corrosion behavior of AISI 304 and 316 stainless steels (SSs) in hot concentrated caustic soda solutions was investigated under heat-transfer conditions. The corrosion potential of the specimens was located in the active region; thus, the alloys
Autor:
Harold C. Templeton
Publikováno v:
Corrosion. 17:9-13
Allowable corrosion rates for equipment with low corrosion tolerance are discussed. Corrosion case histories in the various pulping processes are presented. Sulfite pulping solutions are most frequently-handled in 316 material. Stainless 316 is used
Autor:
F. G. Hammitt, R. Garcia
Publikováno v:
Corrosion. 22:157-167
Cavitation studies have been conducted in lead-bismuth alloy (70 percent lead-30 percent bismuth) at 500 and 1500 F (260–816 C) with a vibratory device utilizing a piezoelectric crystal transducer unit and high-temperature cavitation facility. Test
Publikováno v:
Corrosion. 71:771-783
A test assembly consisting of a coated and scribed aluminum alloy 7075-T6 panel galvanically connected to uncoated through-hole noble fasteners has recently been utilized to quantify corrosion attack during corrosion testing in laboratory chambers. I
Autor:
Gerald S. Frankel, B.C. Rincon Troconis, Longfei Li, W.C. Nickerson, C.A. Matzdorf, R.G. Buchheit
Publikováno v:
Corrosion. 69:1240-1246
A test sample incorporating a coated and scribed Al alloy panel and uncoated through-hole fasteners was designed to provide accelerated response during atmospheric corrosion testing in the field or in laboratory chambers. Protective coatings that wou